Parameter |
Product details |
|||
Product Name: | Bearing steel ball / Chrome steel ball / Steel ball for bearing | |||
Material: |
AISI52100/ GCr15/ 100Cr6/ SUJ2 | |||
SIZE: |
G5 |
G10 |
G40-G200 |
G1000 |
2.381mm-15.875mm |
0.8mm-31.75mm |
4.763mm-100mm |
1.0mm-200mm |
|
HardnessHRC: |
0.8mm-30.0mm |
30.0mm-50.0mm |
50.0mm-200mm |
|
61-66 |
60-65 |
58-64 |
||
Production Standard: |
ISO3290 2001 GB/T308.1-2013 DIN5401-2002 |
Chemical composition of AISI52100 bearing steel balls(GCr15/SUJ2/100Cr6) |
|
C | 0.95% --1.10% |
Si | 0.15%--0.35% |
Mn | 0.25%-0.45% |
P | 0.025% max. |
S | 0.025% max. |
Cr | 1.35% --1.65% |
NI | 0.03%Max |
Mo | 0.1%max |
Bearing steel has high hardness, tensile strength, contact fatigue strength and wear resistance, and considerable toughness, which meets the requirements for corrosion resistance and high temperature resistance under certain conditions.
The high carbon chromium bearing steel has a high carbon content (0.95-1.05%), high and uniform hardness can be obtained after quenching, and a long fatigue life. The disadvantage is that it is slightly less resistant to large loads and impact toughness.
High-carbon chromium bearing steel is mainly used as the rings and rolling elements of rolling bearings under general conditions of use.
Bearing steel balls, as an important part of the bearing, play a very critical role.
Therefore, the use effect and service life of the bearing are closely related to the accuracy and hardness of the bearing steel ball. The hardness of the bearing steel ball is related to the crushing load value of the steel ball.
COUNTRY | STANDARD | MATERIAL NAME |
CHINA | GB | GCr15 |
USA | AISI | E52100 |
JAPAN | JIS | SUJ2 |
GEMANY | DIN | 1.3505 |
The biggest feature of the bearing steel ball is its high hardness and wear resistance. Then we need to be frequently exposed to the hardness value of the steel ball. The hardness value range of the finished steel ball is specified in the national standard of steel ball GB/T 308.1-2013.
<30mm, HRC=61-66;
30MM--50MM, HRC=59-64;
>50MM, HRC=58-64;
After precision washing, oiling & before packing sample balls from the batch are sent for final audit to check for surface roughness, roundness, waviness, lot size variation and hardness in a sophisticated laboratory, according to specified control plans and dock audit procedures. Once all requirements are met, a test certificate is then prepared for the customer. Our sophisticated laboratory is equipped with high precision, worldwide respected machines and equipment and is managed by properly trained and qualified personnel.